FlexiShield WSH paint protection film, 8.0 mil (203 µ) thick, is designed to provide complete surface protection for luxury cars, yachts, architectural interiors and many other personal and commercial goods. FlexiShield WSH has been formulated to offer optimumself-healing performance, durability and installation versatility .
After a decade of field trials in all climatic conditions, from the scorching desert of Arizona to the frozen fjords of Norway, FlexiShield WSH remains the essential choice for the most demanding paint protection film installers.
UV acceleration test – 3000 hours, 105 °F – Passed (equivalent to 5 years)
Special features WSH.
PCE thickness gauge
| Total thickness | 8.0 mils (203 µ)* |
| Top layer | 0.5 mil (13 μ) |
| Polyurethane film | 6.5 mils (165 µ)* |
| Adhesive | 1.0 mil (25 µ) |
Adhesion and peel strength
| Test parameter | Strength (N/m) | Strength (oz/in) | Conditions |
| Peel adhesion | 481.0 N/m | 44 oz/in | 24 hours at room temperature |
| Peeling at 180 degrees | 514.0 N/m | 47 oz/in | 1 week at room temperature |
| 1.0 mil coating | 689.0 N/m | 63 oz/in | 1 week at 160°F/70°C |
| Painted surface | 765.0 N/m | 70 oz/in | 1 week at 95°F/35°C, 95% RH |
Performance indicators
| Test parameter | Result | Conditions |
| TPU Opacity (clarity) ∆ | 1.20% | ASTM D1003-1 Original 0.8 |
| Yellowing ∆ | <1.20% | ASTM D1925-70 |
| Self-repair ∆ | Successful | Laboratory tests |
| Cold shock – Cracking or spalling | Successful | TPJLR.52.055 |
| Elongation (at MD break) | >350% | ASTM 6775-13 |
| Stain-resistant (unleaded gasoline, kerosene) | No aesthetic defects | Laboratory tests |
| Gloss at 20° (stainless steel surface) | >96 GU | 20° glossmeter |
| Chip resistance Gravimeter | No paint damage | ASTM D3170 |