Because every vehicle deserves protection, FlexiShield has developed its new BHP PPF protective film. It features FlexiShield'soutstanding top layer andadhesive, on a more commercial TPU base layer than our STH, WSH, WSHPro and DPH ranges. FlexiShield BHP is our answer to providing excellent protection for all cars, commercial vehicles and commercial fleets in daily use.
FlexiShield BHP is a 7.5 mil (191 µ) thick film featuring a dense topcoat for a harder surface and greater resistance to stains and damage. This film can take a beating and be restored thanks to its built-inthermal self-healing properties.
UV acceleration test – 3000 hours, 105 °F – Passed (equivalent to 5 years)
Special features BHP.
PCE thickness gauge
| Total thickness | 7.8 mils (198 µ)* |
| Top layer | 0.5 mil (13 μ) |
| Polyurethane film | 6.3 mils (160 µ)* |
| Adhesive | 1.0 mil (25 µ) |
Adhesion and peel strength
| Test parameter | Strength (N/m) | Strength (oz/in) | Conditions |
| Peel adhesion | 481.0 N/m | 44 oz/in | 24 hours at room temperature |
| Peeling at 180 degrees | 514.0 N/m | 47 oz/in | 1 week at room temperature |
| 1.0 mil coating | 689.0 N/m | 63 oz/in | 1 week at 160°F/70°C |
| Painted surface | 765.0 N/m | 70 oz/in | 1 week at 95°F/35°C, 95% RH |
Performance indicators
| Test parameter | Result | Conditions |
| TPU Opacity (lightness) ∆ | 1.60% | ASTM D1003-1 Original 0.8 |
| Yellowing ∆ | <2.20% | ASTM D1925-70 |
| Self-repair ∆ | Successful | Laboratory tests |
| Cold shock – Cracking or spalling | Successful | TPJLR.52.055 |
| Elongation (at MD break) | >340% | ASTM 6775-13 |
| Stain-resistant (unleaded gasoline, kerosene) | No aesthetic defects | Laboratory tests |
| Gloss at 20° (stainless steel surface) | >94 GU | 20° glossmeter |
| Chip resistance Gravimeter | No paint damage | ASTM D3170 |